- 缺口沖擊強度: 0.614
- 拉伸強度 [MPa]: 115.0
- 斷裂伸長率 [%]: 168
- 彎曲模量 [MPa]: 9.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.69 g/cc | 1.69 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 115 MPa | 16700 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 2.5 % | 2.5 % | 50 mm/min; ASTM D638 |
| Tensile Modulus | 6.00 GPa | 870 ksi | 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 168 MPa | 24400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 9.00 GPa | 1310 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.614 J/cm | 1.15 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 185 °C @Thickness 3.20 mm | 365 °F @Thickness 0.126 in | Unannealed; ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | |