- 密度 [g/cm3]: 1.4
- 吸水率 [%]: 0.5
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.40 g/cc @Temperature 23.0 °C | 0.0506 lb/in3 @Temperature 73.4 °F | ASTM D1505-68, method C | ||
| Water Absorption | 0.50 % @Temperature 23.0 °C | 0.50 % @Temperature 73.4 °F | 4 days in water; ASTM D570 | ||
| Linear Mold Shrinkage | 0.010 cm/cm @Temperature 150 °C, Time 900 sec | 0.010 in/in @Temperature 302 °F, Time 0.250 hour | DIN 40634 | ||
| Linear Mold Shrinkage, Transverse | 0.0030 cm/cm @Temperature 150 °C, Time 900 sec | 0.0030 in/in @Temperature 302 °F, Time 0.250 hour | DIN 40634 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 150 MPa | 21800 psi | Test speed 100%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2 | ||
| Film Tensile Strength at Yield, TD | 200 MPa | 29000 psi | Test speed 100%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2 | ||
| Film Elongation at Break, MD | >= 200 % | >= 200 % | Test speed 100%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2 | ||
| Film Elongation at Break, TD | 140 % | 140 % | Test speed 100%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2 | ||
| Modulus of Elasticity | 3.60 GPa @Temperature 23.0 °C | 522 ksi @Temperature 73.4 °F | MD; Test speed 1%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2 | ||
| 4.30 GPa @Temperature 23.0 °C | 624 ksi @Temperature 73.4 °F | TD; Test speed 1%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2 | |||
| Coefficient of Friction, Static | 0.40 | 0.40 | DIN 53375 or ASTM D1894 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 2.9 @Frequency 2.40e+8 Hz, Temperature 23.0 °C | 2.9 @Frequency 2.40e+8 Hz, Temperature 73.4 °F | DIN 40634 or VDE 0345 in air | ||
| 2.9 @Frequency 9.30e+9 Hz, Temperature 23.0 °C | 2.9 @Frequency 9.30e+9 Hz, Temperature 73.4 °F | DIN 40634 or VDE 0345 in air | |||
| 3.2 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 3.2 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | DIN 40634 or VDE 0345 in air | |||
| 3.3 @Frequency 50.0 Hz, Temperature 23.0 °C | 3.3 @Frequency 50.0 Hz, Temperature 73.4 °F | DIN 40634 or VDE 0345 in air | |||
| 3.3 @Frequency 1000 Hz, Temperature 23.0 °C | 3.3 @Frequency 1000 Hz, Temperature 73.4 °F | DIN 40634 or VDE 0345 in air | |||
| 3.6 @Frequency 50.0 Hz, Temperature 150 °C | 3.6 @Frequency 50.0 Hz, Temperature 302 °F | DIN 40634 or VDE 0345 in air | |||
| Dielectric Strength | 450 kV/mm @Temperature 23.0 °C | 11400 kV/in @Temperature 73.4 °F | DC; DIN 40634 or VDE 0345 in air | ||
| 135 kV/mm @Frequency 50.0 Hz, Temperature 150 °C | 3430 kV/in @Frequency 50.0 Hz, Temperature 302 °F | DIN 40634 or VDE 0345 in air | |||
| 150 kV/mm @Frequency 50.0 Hz, Temperature 23.0 °C | 3810 kV/in @Frequency 50.0 Hz, Temperature 73.4 °F | DIN 40634 or VDE 0345 in air | |||
| Optical Properties | Metric | English | Comments | ||
| Haze | 25 % | 25 % | Enlarged measurement angle; ASTM D1003-61, method A | ||
| Descriptive Properties | |||||
| Conductivity of Aqueous Extract (μS/cm) | 2 | DIN 40634 or VDE 0345; 1 kHz | |||
| F5-value (MPa) | 105 | ISO 527-1, ISO 527-3; Sample type 2; MD; Test speed 100%/min.; 23oC, 50% r.h. | |||
| 105 | ISO 527-1, ISO 527-3; Sample type 2; TD; Test speed 100%/min.; 23oC, 50% r.h. | ||||
| Frigen Extract (%) | 0.05 | DIN 8944; Cold extraction | |||
| Trichloroethylene- Extract (%) | 0.2 | DIN 8943; Extracted in Soxhalet apparatus for 2h. Boiled down for 15h at 105oC | |||