- 密度 [g/cm3]: 1.19
- 缺口沖擊強(qiáng)度: 5.2
- 彎曲模量 [MPa]: 2.10
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in3 | ASTM D792 |
| Linear Mold Shrinkage | 0.0080 - 0.010 cm/cm | 0.0080 - 0.010 in/in | 3.2 mm; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 45.0 MPa | 6530 psi | 5 mm/min; ASTM D638 |
| Flexural Strength | 70.0 MPa | 10200 psi | 1.3 mm/min; ASTM D790 |
| Flexural Modulus | 2.10 GPa | 305 ksi | 1.3 mm/min; ASTM D790 |
| Izod Impact, Notched | 5.20 J/cm @Temperature 23.0 °C | 9.74 ft-lb/in @Temperature 73.4 °F | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Feed Temperature | 245 - 255 °C | 473 - 491 °F | |
| Middle Barrel Temperature | 250 - 260 °C | 482 - 500 °F | |
| Front Barrel Temperature | 255 - 265 °C | 491 - 509 °F | |
| Nozzle Temperature | 260 - 270 °C | 500 - 518 °F | |
| Melt Temperature | 260 - 275 °C | 500 - 527 °F | |
| Mold Temperature | 18.0 - 75.0 °C | 64.4 - 167 °F | |
| Injection Pressure | 69.0 - 138 MPa | 10000 - 20000 psi | |