- 拉伸強(qiáng)度 [MPa]: 51.7
- 彎曲模量 [MPa]: 2.24
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.33 g/cc | 1.33 g/cc | |||
| Viscosity Measurement | >= 0.66 | >= 0.66 | Intrinsic Viscosity; ASTM D3835 | ||
| Thickness | 229 - 1140 microns | 9.00 - 45.0 mil | |||
| Linear Mold Shrinkage | 0.020 - 0.050 cm/cm | 0.020 - 0.050 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 51.7 - 58.6 MPa | 7500 - 8500 psi | ASTM D638 | ||
| Elongation at Break | 100 - 300 % | 100 - 300 % | ASTM D638 | ||
| Flexural Modulus | 2.24 - 2.55 GPa | 325 - 370 ksi | ASTM D790 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 65.6 °C | 150 °F | |||
| Minimum Service Temperature, Air | -17.8 °C | 0.000 °F | |||
| Optical Properties | Metric | English | Comments | ||
| Haze | <= 4.0 % | <= 4.0 % | ASTM D1003 | ||
| Transmission, Visible | >= 85 % | >= 85 % | ASTM D1003 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 121 - 154 °C | 250 - 310 °F | Thermoforming Temp | ||
| Descriptive Properties | |||||
| Clarity, % | >97 | ||||
| Resistance to Acid | Good to Excellent | ||||
| Resistance to Alcohols | Good to Excellent | ||||
| Resistance to Alkalis | Fair to Good | ||||
| Resistance to Fat, Grease, and Oil | Good to Excellent | ||||
| Resistance to Hydrocarbon Solvents | Good to Excellent | ||||
| Resistance to Strong Oxidizers | Good to Excellent | ||||
| Yield, in2/lb/mil | 20810 | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.