- 密度 [g/cm3]: 1.33
- 缺口沖擊強度: 1.82
- 斷裂伸長率 [%]: 110
- 彎曲模量 [MPa]: 3.65
- 熱變形溫度 [℃]: 223.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in3 | ISO 1183 & ASTM D792 |
| Linear Mold Shrinkage | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 67.6 MPa | 9800 psi | ASTM D638 |
| 73.0 MPa | 10600 psi | 5 mm/min; ISO 527-2/1A | |
| Elongation at Break | 3.0 % | 3.0 % | 5 mm/min; ISO 527-2/1A |
| Tensile Modulus | 4.27 GPa | 620 ksi | ASTM D638 |
| 4.80 GPa | 696 ksi | 1 mm/min; ISO 527-2/1A | |
| Flexural Strength | 115 MPa | 16700 psi | ISO 178 |
| Flexural Yield Strength | 110 MPa | 16000 psi | ASTM D790 |
| Flexural Modulus | 3.65 GPa | 530 ksi | ASTM D790 |
| 4.20 GPa | 609 ksi | ISO 178 | |
| Izod Impact, Notched | 1.82 J/cm | 3.40 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 18.0 kJ/m2 | 8.57 ft-lb/in2 | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m2 | 14.3 ft-lb/in2 | ISO 180/1U |
| Charpy Impact Unnotched | 5.30 J/cm2 | 25.2 ft-lb/in2 | ISO 179/1eU |
| 3.80 J/cm2 @Temperature -30.0 °C | 18.1 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 1.60 J/cm2 | 7.61 ft-lb/in2 | ISO 179/1eA |
| 0.840 J/cm2 @Temperature -30.0 °C | 4.00 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | |
| Electrical Properties | Metric | English | Comments |
| Dielectric Strength | 19.3 kV/mm | 490 kV/in | Short Term; ASTM D149 |
| Arc Resistance | 120 sec | 120 sec | ASTM D495 |
| Comparative Tracking Index | 400 V | 400 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 30.0 μm/m-°C @Temperature 20.0 °C | 16.7 μin/in-°F @Temperature 68.0 °F | ISO 11359-2 |
| Melting Point | 250 °C | 482 °F | ISO 11357-1,2,3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 223 °C | 433 °F | ASTM D648 |
| 236 °C | 457 °F | ISO 75-1, -2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | ASTM D648 |
| 141 °C | 286 °F | ISO 75-1, -2 | |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 260 - 270 °C | 500 - 518 °F | |
| Middle Barrel Temperature | 270 - 280 °C | 518 - 536 °F | |
| Front Barrel Temperature | 280 - 285 °C | 536 - 545 °F | |
| Nozzle Temperature | 270 - 290 °C | 518 - 554 °F | |
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |
| Mold Temperature | 130 °C | 266 °F | |
| Back Pressure | 0.552 MPa | 80.0 psi | |