- 密度 [g/cm3]: 1.72
- 吸水率 [%]: 0.06
- 缺口沖擊強度: 0.7
- 彎曲強度 [MPa]: 140.0
- 彎曲模量 [MPa]: 15.6
- 熱變形溫度 [℃]: 245.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.72 g/cc | 0.0621 lb/in3 | ISO 1183 |
| Water Absorption | 0.060 % | 0.060 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 140 MPa | 20300 psi | ISO 527 |
| Elongation at Break | 1.4 % | 1.4 % | ASTM D638 |
| Flexural Strength | 215 MPa | 31200 psi | ISO 178 |
| Flexural Modulus | 15.6 GPa | 2260 ksi | ISO 178 |
| Izod Impact, Notched | 0.700 J/cm | 1.31 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 3.9 @Frequency 100000 Hz | 3.9 @Frequency 100000 Hz | ASTM D150 |
| Dielectric Strength | 17.0 kV/mm @Thickness 3.17 mm | 432 kV/in @Thickness 0.125 in | ASTM D149 |
| Dissipation Factor | 0.010 @Frequency 100000 Hz | 0.010 @Frequency 100000 Hz | ASTM D150 |
| Arc Resistance | 126 sec | 126 sec | ASTM D495 |
| Comparative Tracking Index | 200 V | 200 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 30.6 μm/m-°C @Temperature 20.0 °C | 17.0 μin/in-°F @Temperature 68.0 °F | Flow Direction; ASTM E831 |
| CTE, linear, Transverse to Flow | 103 μm/m-°C @Temperature 20.0 °C | 57.2 μin/in-°F @Temperature 68.0 °F | ASTM E831 |
| Melting Point | 248 °C | 478 °F | DSC; ISO 3146 |
| Deflection Temperature at 0.46 MPa (66 psi) | 245 °C | 473 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 228 °C | 442 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 270 - 280 °C | 518 - 536 °F | Injection; barrel center zone temperature |