- 熔體流動速率 [g/10min]: 6.0
- 缺口沖擊強度: 6.41
- 拉伸強度 [MPa]: 54.0
- 彎曲模量 [MPa]: 2.139
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.21 g/cc | 1.21 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0070 - 0.0090 cm/cm | 0.0070 - 0.0090 in/in | ASTM D955 |
| Melt Flow | 6.0 g/10 min @Load 3.80 kg, Temperature 230 °C | 6.0 g/10 min @Load 8.38 lb, Temperature 446 °F | ASTM D1238 |
| 12 g/10 min @Load 2.16 kg, Temperature 265 °C | 12 g/10 min @Load 4.76 lb, Temperature 509 °F | ASTM D1238 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 54.0 MPa | 7830 psi | chs 2.0 in/min; ASTM D638 |
| Elongation at Yield | 4.6 % | 4.6 % | chs 2.0 in/min; ASTM D638 |
| Flexural Strength | 80.6 MPa | 11700 psi | chs 0.05 in/min; at yield; ASTM D790 |
| Flexural Modulus | 2.139 GPa | 310.2 ksi | chs 0.05 in/min; ASTM D790 |
| Izod Impact, Notched | 6.41 J/cm @Thickness 3.17 mm | 12.0 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 128 °C @Load 1.00 kg, Thickness 3.17 mm | 262 °F @Load 2.20 lb, Thickness 0.125 in | ASTM D1527 |