- 熔體流動速率 [g/10min]: 35.0
- 吸水率 [%]: 0.15
- 缺口沖擊強度: 8.01
- 拉伸強度 [MPa]: 58.6
- 彎曲模量 [MPa]: 2.19
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Water Absorption | 0.15 % | 0.15 % | 24 hours at 73°F; ASTM D570 |
| Water Absorption at Saturation | 0.35 % | 0.35 % | 73°F; ASTM D570 |
| Linear Mold Shrinkage | 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in | ASTM D955 |
| Melt Flow | 35 g/10 min @Load 1.20 kg, Temperature 300 °C | 35 g/10 min @Load 2.65 lb, Temperature 572 °F | Procedure A Condition 0; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 55.8 MPa | 8100 psi | chs 2 in/min; ASTM D638 |
| Tensile Strength, Yield | 58.6 MPa | 8500 psi | chs 2 in/min; ASTM D638 |
| Elongation at Break | 100 % | 100 % | ASTM D638 |
| Flexural Modulus | 2.19 GPa | 318 ksi | Tangent (chs speed 0.05 in/min); ASTM D790 |
| Izod Impact, Notched | 8.01 J/cm | 15.0 ft-lb/in | Test Method A (0.125 in bar); ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 220 °F | 0.125 in bar, Unannealed/Conditioned 48 hours; ASTM D648 |