- 熔體流動(dòng)速率 [g/10min]: 21.0
- 密度 [g/cm3]: 1.3
- 拉伸強(qiáng)度 [MPa]: 45.0
- 熱變形溫度 [℃]: 101.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in3 | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.0090 cm/cm | 0.0090 in/in | parallel; ISO 294-4, 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | ISO 294-4, 2577 | ||
| Melt Flow | 21 g/10 min @Load 5.00 kg, Temperature 260 °C | 21 g/10 min @Load 11.0 lb, Temperature 500 °F | Estimated using room temperature density; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 40.0 MPa | 5800 psi | ISO 527-1/-2 | ||
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | ISO 527-1/-2 | ||
| Elongation at Break | 17 % | 17 % | Nominal; ISO 527-1/-2 | ||
| Elongation at Yield | 2.8 % | 2.8 % | ISO 527-1/-2 | ||
| Tensile Modulus | 2.60 GPa | 377 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 2.9 @Frequency 1.00e+6 Hz | 2.9 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 3.3 @Frequency 100 Hz | 3.3 @Frequency 100 Hz | IEC 60250 | |||
| Dissipation Factor | 0.014 @Frequency 1.00e+6 Hz | 0.014 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 0.025 @Frequency 100 Hz | 0.025 @Frequency 100 Hz | IEC 60250 | |||
| Comparative Tracking Index | 300 V | 300 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 80.0 μm/m-°C | 44.4 μin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 100 μm/m-°C | 55.6 μin/in-°F | ISO 11359-1/-2 | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 101 °C | 214 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 8.0 MPa | 61.0 °C | 142 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | V-0 @Thickness 0.750 mm | V-0 @Thickness 0.0295 in | IEC 60695-11-10 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 260 °C | 500 °F | Injection Molding; ISO 294 | ||
| Mold Temperature | 80.0 °C | 176 °F | Injection Molding; ISO 10724 | ||
| Descriptive Properties | |||||
| ISO Shortname | ISO 7792-1-PBT+PC,GFHLMPR,09-020; ISO1043-(PBT+PC) FR(17) | ||||
| Region | Asia Pacific | ||||
| Europe | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||