- 熔體流動速率 [g/10min]: 25.0
- 密度 [g/cm3]: 1.65
- 吸水率 [%]: 0.4
- 熱變形溫度 [℃]: 220.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.65 g/cc | 0.0596 lb/in3 | ISO 1183 | ||
| Water Absorption | 0.40 % | 0.40 % | Test Sim. to ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | 23°C/50% R.H.; Test Sim. to ISO 62 | ||
| Viscosity Test | 93 cm3/g | 93 cm3/g | Viscosity number; ISO 307, 1157, 1628 | ||
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | parallel; ISO 294-4, 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.0012 cm/cm | 0.0012 in/in | ISO 294-4, 2577 | ||
| Melt Flow | 25 g/10 min @Load 2.16 kg, Temperature 260 °C | 25 g/10 min @Load 4.76 lb, Temperature 500 °F | Estimated using room temperature density; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 130 MPa | 18900 psi | ISO 527-1/-2 | ||
| Elongation at Break | 2.0 % | 2.0 % | ISO 527-1/-2 | ||
| Tensile Modulus | 10.5 GPa | 1520 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | 5.00 J/cm2 @Temperature -30.0 °C | 23.8 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eU | ||
| 5.00 J/cm2 @Temperature 23.0 °C | 23.8 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | <= 1.00 J/cm2 @Temperature -30.0 °C | <= 4.76 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | ||
| <= 1.00 J/cm2 @Temperature 23.0 °C | <= 4.76 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |||
| Tensile Creep Modulus, 1 hour | 11000 MPa | 1.60e+6 psi | ISO 899-1 | ||
| Tensile Creep Modulus, 1000 hours | 10000 MPa | 1.45e+6 psi | ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Constant | 3.9 @Frequency 1.00e+6 Hz | 3.9 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 4.0 @Frequency 100 Hz | 4.0 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 29.0 kV/mm | 737 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.0050 @Frequency 100 Hz | 0.0050 @Frequency 100 Hz | IEC 60250 | ||
| 0.016 @Frequency 1.00e+6 Hz | 0.016 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 175 V | 175 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 20.0 μm/m-°C | 11.1 μin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 80.0 μm/m-°C | 44.4 μin/in-°F | ISO 11359-1/-2 | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75-1/-2 | ||
| Vicat Softening Point | 210 °C | 410 °F | 50°C/h 50N; ISO 306 | ||
| Flammability, UL94 | V-0 @Thickness 0.750 mm | V-0 @Thickness 0.0295 in | IEC 60695-11-10 | ||
| V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | IEC 60695-11-10 | |||
| V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | IEC 60695-11-20 | |||
| Oxygen Index | 32 % | 32 % | ISO 4589-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 260 °C | 500 °F | Injection Molding; ISO 294 | ||
| Mold Temperature | 80.0 °C | 176 °F | Injection Molding; ISO 10724 | ||
| Descriptive Properties | |||||
| Form | Pellets | ||||
| ISO Shortname | ISO 7792-1-PBT,GFHMR,07-100,GF30; ISO 1043-PBT GF FR(17) | ||||
| Processing | Injection molding | ||||
| Region | Asia Pacific | ||||
| Europe | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||