- 熔體流動速率 [g/10min]: 26.72
- 密度 [g/cm3]: 1.67
- 缺口沖擊強度: 10.0
- 彎曲模量 [MPa]: 10.0
- 熱變形溫度 [℃]: 215.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.700 g/cc | 0.0253 lb/in3 | ISO 60 |
| Density | 1.67 g/cc | 0.0603 lb/in3 | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | 60x60x2; 260°C / MT 80°C; 600 bar; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm | 0.011 in/in | 60x60x2; 260°C / MT 80°C; 600 bar; ISO 294-4 |
| Melt Flow | 26.72 g/10 min @Load 2.16 kg, Temperature 260 °C | 26.72 g/10 min @Load 4.76 lb, Temperature 500 °F | ISO 1133-1 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 120 MPa | 17400 psi | 5 mm/min; ISO 527-1,-2 |
| Elongation at Break | 2.0 % | 2.0 % | 5 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 9.80 GPa | 1420 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Strength | 185 MPa | 26800 psi | 2 mm/min; ISO 178-A |
| Flexural Modulus | 10.0 GPa | 1450 ksi | 2 mm/min; ISO 178-A |
| Izod Impact, Notched (ISO) | <= 10.0 kJ/m2 @Temperature 23.0 °C | <= 4.76 ft-lb/in2 @Temperature 73.4 °F | ISO 180-1A |
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m2 @Temperature 23.0 °C | 16.7 ft-lb/in2 @Temperature 73.4 °F | ISO 180-1U |
| Charpy Impact Unnotched | 4.00 J/cm2 @Temperature 23.0 °C | 19.0 ft-lb/in2 @Temperature 73.4 °F | ISO 179-1eU |
| Charpy Impact, Notched | <= 1.00 J/cm2 @Temperature 23.0 °C | <= 4.76 ft-lb/in2 @Temperature 73.4 °F | ISO 179-1eA |
| Electrical Properties | Metric | English | Comments |
| Dielectric Strength | 29.8 kV/mm | 757 kV/in | IEC 60243-1 |
| Comparative Tracking Index | 175 - 250 V | 175 - 250 V | Solution A; UL 746A |
| 225 V | 225 V | Solution A; IEC 60112 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 30.0 μm/m-°C @Temperature 23.0 - 55.0 °C | 16.7 μin/in-°F @Temperature 73.4 - 131 °F | ISO 11359-1,-2 |
| CTE, linear, Transverse to Flow | 100 μm/m-°C @Temperature 23.0 - 55.0 °C | 55.6 μin/in-°F @Temperature 73.4 - 131 °F | ISO 11359-1,-2 |
| Melting Point | 225 °C | 437 °F | 10 °C/min; ISO 11357-1,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | ISO 75-1,-2 |
| Flammability, UL94 | V-0 @Thickness 0.400 mm | V-0 @Thickness 0.0157 in | |
| V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | ||
| V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | ||
| V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | ||
| Oxygen Index | 36.4 % | 36.4 % | Method A; ISO 4589-2 |
| Glow Wire Test | 725 °C @Thickness 1.50 mm | 1340 °F @Thickness 0.0591 in | GWIT; IEC 60695-2-13 |
| 725 °C @Thickness 3.00 mm | 1340 °F @Thickness 0.118 in | GWIT; IEC 60695-2-13 | |
| 850 °C @Thickness 0.800 mm | 1560 °F @Thickness 0.0315 in | GWIT; IEC 60695-2-13 | |
| 900 °C @Thickness 0.400 mm | 1650 °F @Thickness 0.0157 in | GWIT; IEC 60695-2-13 | |
| 960 °C @Thickness 0.400 mm | 1760 °F @Thickness 0.0157 in | GWFI; IEC 60695-2-12 | |
| 960 °C @Thickness 0.800 mm | 1760 °F @Thickness 0.0315 in | GWFI; IEC 60695-2-12 | |
| 960 °C @Thickness 1.50 mm | 1760 °F @Thickness 0.0591 in | GWFI; IEC 60695-2-12 | |
| 960 °C @Thickness 3.00 mm | 1760 °F @Thickness 0.118 in | GWFI; IEC 60695-2-12 | |
| Shrinkage | 0.10 % | 0.10 % | post-shrinkage, 60x60x2; 120°C; 4 h; ISO 294-4 |
| 0.10 % | 0.10 % | post-shrinkage, transverse, 60x60x2; 120°C; 4 h; ISO 294-4 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 250 °C | 482 °F | Injection molding; ISO 294 |
| Mold Temperature | 80.0 °C | 176 °F | Injection molding; ISO 294 |
| Dry Time | 4.00 - 8.00 hour @Temperature 120 °C | 4.00 - 8.00 hour @Temperature 248 °F | |
| Moisture Content | 0.00 - 0.020 % | 0.00 - 0.020 % | Karl Fischer test |