- 缺口沖擊強度: 0.78
- 彎曲模量 [MPa]: 8.826
- 硬度: 120.0
- 熱變形溫度 [℃]: 225.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.63 g/cc | 1.63 g/cc | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.050 % | 0.050 % | 60% RH; ASTM D570 |
| Linear Mold Shrinkage | 0.0070 - 0.010 cm/cm | 0.0070 - 0.010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength | 132 MPa | 19100 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Flexural Strength | 206 MPa | 29900 psi | ASTM D790 |
| Flexural Modulus | 8.826 GPa | 1280 ksi | ASTM D790 |
| Izod Impact, Notched | 0.780 J/cm | 1.46 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 3.7 | 3.7 | ASTM D150 |
| Dielectric Strength | 27.0 kV/mm | 686 kV/in | ASTM D149 |
| Arc Resistance | 110 sec | 110 sec | ASTM D495 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 40.0 μm/m-°C | 22.2 μin/in-°F | ASTM D696 |
| Melting Point | 224 °C | 435 °F | ASTM D1525 |
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C | 437 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | |