- 吸水率 [%]: 0.06
- 缺口沖擊強度: 0.55
- 彎曲模量 [MPa]: 2.80
- 硬度: 119.0
- 熱變形溫度 [℃]: 195.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.41 g/cc @Temperature 23.0 °C | 1.41 g/cc @Temperature 73.4 °F | ASTM D792 | ||
| Water Absorption | 0.060 % @Temperature 23.0 °C, Time 86400 sec | 0.060 % @Temperature 73.4 °F, Time 24.0 hour | ASTM D570 | ||
| Linear Mold Shrinkage | 0.0090 - 0.011 cm/cm @Temperature 23.0 °C | 0.0090 - 0.011 in/in @Temperature 73.4 °F | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 119 | 119 | ASTM D785 | ||
| Tensile Strength at Break | 50.0 MPa | 7250 psi | 10mm/min; ASTM D638 | ||
| Elongation at Break | 12 % | 12 % | 10mm/min; ASTM D638 | ||
| Flexural Strength | 70.0 MPa | 10200 psi | 2mm/min; ASTM D790 | ||
| Flexural Modulus | 2.80 GPa | 406 ksi | 2mm/min; ASTM D790 | ||
| Izod Impact, Notched | 0.550 J/cm @Thickness 3.20 mm, Temperature 23.0 °C | 1.03 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F | ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C @Thickness 6.40 mm | 383 °F @Thickness 0.252 in | ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C @Thickness 6.40 mm | 221 °F @Thickness 0.252 in | ASTM D648 | ||
| Flammability, UL94 | HB @Thickness 1.50 - 1.65 mm | HB @Thickness 0.0591 - 0.0650 in | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | <= 270 °C | <= 518 °F | |||
| Rear Barrel Temperature | 220 - 240 °C | 428 - 464 °F | Start Point: 230°C | ||
| Middle Barrel Temperature | 230 - 250 °C | 446 - 482 °F | Start Point: 240°C | ||
| Front Barrel Temperature | 240 - 260 °C | 464 - 500 °F | Start Point: 250°C | ||
| Melt Temperature | 240 - 260 °C | 464 - 500 °F | Start Point: 250°C | ||
| Mold Temperature | 50.0 - 80.0 °C | 122 - 176 °F | Start Point: 60°C | ||
| Drying Temperature | 120 - 140 °C @Time 10800 - 18000 sec | 248 - 284 °F @Time 3.00 - 5.00 hour | Pre-dry | ||
| Descriptive Properties | |||||
| Injection Speed | Moderate to High | ||||
| Mineral Content (%) | 15 | ||||