- 密度 [g/cm3]: 1.21
- 吸水率 [%]: 0.3
- 拉伸強度 [MPa]: 45.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in3 | GB/1033 | ||
| Water Absorption | 0.30 % | 0.30 % | GB/T1034 | ||
| Linear Mold Shrinkage | 0.0070 cm/cm | 0.0070 in/in | GB/15585 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | GB/1040 | ||
| Flexural Strength | 78.0 MPa | 11300 psi | GB/9341 | ||
| Charpy Impact Unnotched | NB | NB | IS0179-1:2000 | ||
| Charpy Impact, Notched | 6.00 J/cm2 | 28.6 ft-lb/in2 | IS0179-1:2000 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | D257 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 - 110 °C | 176 - 230 °F | GB/1634 | ||
| Flammability, UL94 | HB - V-0 | HB - V-0 | GB/T2408 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 230 - 280 °C | 446 - 536 °F | |||
| Dry Time | 5 hour | 5 hour | Chute Hot-Wind, 100°C | ||
| 8 hour | 8 hour | Horizontal Oven, 100°C | |||
| Injection Pressure | 60.0 - 120 MPa | 8700 - 17400 psi | |||
| Descriptive Properties | |||||
| Chromatism (?E) | =0.8 | ||||
| Granule Diameter | Φ3x3-5 | ||||
| Low Temp Tenacity (-20°C) | Good (Keep 80% of the original impact strength) | ||||
| Speed of Shoot, % | 35-80 | ||||
| Surface Polish | High | ||||