- 熔體流動速率 [g/10min]: 8.61
- 密度 [g/cm3]: 1.23
- 吸水率 [%]: 0.6
- 拉伸強度 [MPa]: 40.0
- 熱變形溫度 [℃]: 145.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in3 | ISO 1183 |
| Water Absorption at Saturation | 0.60 % | 0.60 % | ISO 62 |
| Melt Flow | 8.61 g/10 min @Load 2.16 kg, Temperature 250 °C | 8.61 g/10 min @Load 4.76 lb, Temperature 482 °F | ISO 1133 |
| 19.68 g/10 min @Load 5.00 kg, Temperature 250 °C | 19.68 g/10 min @Load 11.0 lb, Temperature 482 °F | ISO 1133 | |
| 73.8 g/10 min @Load 10.0 kg, Temperature 260 °C | 73.8 g/10 min @Load 22.0 lb, Temperature 500 °F | ISO 1133 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 70 | 70 | ISO 868 |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | ISO 527-1/2 |
| Elongation at Break | 40 % | 40 % | ISO 527-1/2 |
| Elongation at Yield | 3.8 % | 3.8 % | ISO 527-1/2 |
| Tensile Modulus | 1.75 GPa | 254 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179/1eU |
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 1.20 J/cm2 @Temperature -30.0 °C | 5.71 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA |
| 1.50 J/cm2 @Temperature 23.0 °C | 7.14 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 140 μm/m-°C @Temperature 23.0 - 80.0 °C | 77.8 μin/in-°F @Temperature 73.4 - 176 °F | Longitudinal; ISO 11359, DIN 53752 |
| CTE, linear, Transverse to Flow | 140 μm/m-°C @Temperature 23.0 - 80.0 °C | 77.8 μin/in-°F @Temperature 73.4 - 176 °F | ISO 11359, DIN 53752 |
| Deflection Temperature at 0.46 MPa (66 psi) | 145 °C | 293 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ISO 75-1/-2 |
| Vicat Softening Point | 145 °C | 293 °F | Method B, 50 N; ISO 306 |
| 215 °C | 419 °F | Method A, 10 N; ISO 306 | |