- 熔體流動速率 [g/10min]: 61.79
- 密度 [g/cm3]: 1.67
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.67 g/cc | 0.0603 lb/in3 | ISO 1183 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | Post Shrinkage (5 h, 140°C) on 2 mm sheets with film gate at rim, mold temperature 80°C |
| 0.013 cm/cm @Thickness 2.00 mm | 0.013 in/in @Thickness 0.0787 in | sheet with film gate at rim, mold temperature 80°C | |
| Linear Mold Shrinkage, Transverse | 0.0030 cm/cm | 0.0030 in/in | Post Shrinkage (5 h, 140°C) on 2 mm sheets with film gate at rim, mold temperature 80°C |
| 0.014 cm/cm | 0.014 in/in | ||
| Melt Flow | 61.79 g/10 min @Load 2.16 kg, Temperature 250 °C | 61.79 g/10 min @Load 4.76 lb, Temperature 482 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 44.0 MPa | 6380 psi | ISO 527-1/2 |
| Elongation at Break | 1.1 % | 1.1 % | ISO 527-1/2 |
| Tensile Modulus | 4.80 GPa | 696 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | 1.50 J/cm2 @Temperature 23.0 °C | 7.14 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU |
| Charpy Impact, Notched | 0.210 J/cm2 @Temperature 23.0 °C | 0.999 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| Flammability, UL94 | V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | IEC 60695 |
| V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | IEC 60695 | |