- 密度 [g/cm3]: 1.74
- 吸水率 [%]: 0.11
- 缺口沖擊強度: 6.2
- 彎曲強度 [MPa]: 85.0
- 彎曲模量 [MPa]: 8.50
- 熱變形溫度 [℃]: 221.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.74 g/cc | 0.0629 lb/in3 | ASTM D792 |
| Water Absorption | 0.11 % | 0.11 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 50 | 50 | ISO 2039-2 |
| Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | ISO 527 |
| Elongation at Break | 2.3 % | 2.3 % | ASTM D638 |
| Flexural Strength | 125 MPa | 18100 psi | ISO 178 |
| Flexural Modulus | 8.50 GPa | 1230 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 6.20 kJ/m2 | 2.95 ft-lb/in2 | ISO 180/1A |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 17.0 kV/mm @Thickness 3.17 mm | 432 kV/in @Thickness 0.125 in | 50% RH; ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 221 °C | 430 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 387 °F | ISO 75 |
| Flammability, UL94 | V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | UL94 |