- 密度 [g/cm3]: 1.46
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in3 | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.0180 - 0.0200 cm/cm | 0.0180 - 0.0200 in/in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 155 | 155 | ISO 2039-2 | ||
| Tensile Strength at Break | 58.0 MPa | 8410 psi | 5mm/min; ISO 527-2/1A | ||
| Elongation at Break | 8.00 % | 8.00 % | 5mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 3.20 GPa | 464 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 86.0 MPa | 12500 psi | ISO 178 | ||
| Charpy Impact Unnotched | 3.30 J/cm2 | 15.7 ft-lb/in2 | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.350 J/cm2 | 1.67 ft-lb/in2 | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | 400 V | 400 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 63.0 °C | 145 °F | ISO 75-1, -2 | ||
| Flammability, UL94 | HB @Thickness 0.790 mm | HB @Thickness 0.0311 in | UL94 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| 65.0 - 93.0 °C | 149 - 199 °F | Cavity temperature | |||
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Rear Barrel Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Middle Barrel Temperature | 235 - 250 °C | 455 - 482 °F | |||
| Front Barrel Temperature | 240 - 260 °C | 464 - 500 °F | |||
| Nozzle Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |||
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 4 | 240 - 260 °C | 464 - 500 °F | |||
| Die Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Melt Temperature | 235 - 260 °C | 455 - 500 °F | |||
| 235 - 260 °C | 455 - 500 °F | ||||
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |||
| Back Pressure | 0.000 - 0.345 MPa | 0.000 - 50.0 psi | |||
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Descriptive Properties | |||||
| Processing Notes | Fast Injection Speed | ||||
| Medium Screw Speed | |||||