- 熔體流動(dòng)速率 [g/10min]: 17.0
- 密度 [g/cm3]: 1.35
- 缺口沖擊強(qiáng)度: 3.8
- 拉伸強(qiáng)度 [MPa]: 79.3
- 彎曲模量 [MPa]: 3.55
- 熱變形溫度 [℃]: 206.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | ASTM D792 | ||
| Density | 1.35 g/cc | 0.0488 lb/in3 | ISO 1183 | ||
| Density of Compound | 1.11 g/cc | 0.0401 lb/in3 | melt; Internal | ||
| Moisture Absorption | 0.200 % | 0.200 % | 23°C/50%RH; ISO 62 | ||
| Viscosity Test | 145 cm3/g | 145 cm3/g | ISO 307, 1157, 1628 | ||
| Linear Mold Shrinkage, Flow | 0.00600 - 0.0100 cm/cm | 0.00600 - 0.0100 in/in | ASTM D955 | ||
| 0.00600 - 0.0100 cm/cm | 0.00600 - 0.0100 in/in | ISO 294-4 | |||
| Linear Mold Shrinkage, Transverse | 0.0100 - 0.0140 cm/cm | 0.0100 - 0.0140 in/in | ISO 294-4 | ||
| Melt Flow | 17.0 g/10 min | 17.0 g/10 min | ASTM D1238 | ||
| 18.0 g/10 min @Load 2.16 kg, Temperature 250 °C | 18.0 g/10 min @Load 4.76 lb, Temperature 482 °F | (MVR) cm3/10min; ISO 1133 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 66.9 MPa | 9700 psi | ASTM D638 | ||
| 78.0 MPa | 11300 psi | 5mm/min; ISO 527-2/1A | |||
| Tensile Strength, Yield | 79.3 MPa | 11500 psi | ASTM D638 | ||
| Elongation at Break | 8.00 % | 8.00 % | 5mm/min; ISO 527-2/1A | ||
| 8.50 % @Temperature 22.8 °C | 8.50 % @Temperature 73.0 °F | ASTM D638 | |||
| Tensile Modulus | 3.10 GPa @Temperature 22.8 °C | 450 ksi @Temperature 73.0 °F | ASTM D638 | ||
| Flexural Strength | 105 MPa | 15200 psi | ISO 178 | ||
| 110 MPa | 16000 psi | ASTM D790 | |||
| Flexural Modulus | 3.55 GPa | 515 ksi | ISO 178 | ||
| 3.45 GPa @Temperature 22.8 °C | 500 ksi @Temperature 73.0 °F | ASTM D790 | |||
| Izod Impact, Notched (ISO) | 3.80 kJ/m2 | 1.81 ft-lb/in2 | ISO 180/1A | ||
| Izod Impact, Unnotched (ISO) | 23.0 kJ/m2 | 10.9 ft-lb/in2 | ISO 180/1U | ||
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU | ||
| 19.0 J/cm2 @Temperature -30.0 °C | 90.4 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.600 J/cm2 | 2.86 ft-lb/in2 | ISO 179/1eA | ||
| 0.550 J/cm2 @Temperature -30.0 °C | 2.62 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 | |||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Constant | 3.60 @Frequency 1.00e+6 Hz | 3.60 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 4.00 @Frequency 100 Hz | 4.00 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 18.5 kV/mm | 470 kV/in | short term; ASTM D149 | ||
| 23.0 kV/mm | 584 kV/in | IEC 60243-1 | |||
| Dissipation Factor | 0.00130 @Frequency 100 Hz | 0.00130 @Frequency 100 Hz | IEC 60250 | ||
| 0.0200 @Frequency 1.00e+6 Hz | 0.0200 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Arc Resistance | 130 sec | 130 sec | ASTM D495 | ||
| Comparative Tracking Index | 250 V | 250 V | ASTM D3638 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 130 μm/m-°C | 72.2 μin/in-°F | ISO 11359-2 | ||
| Specific Heat Capacity | 1.97 J/g-°C | 0.471 BTU/lb-°F | Internal | ||
| Thermal Conductivity | 0.131 W/m-K | 0.909 BTU-in/hr-ft2-°F | Internal | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| 225 °C | 437 °F | ASTM D3418 | |||
| Transformation Temperature, Tg | 60.0 °C | 140 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 206 °C | 403 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 143 °C | 289 °F | ISO 75-1, -2 | ||
| Vicat Softening Point | 185 °C | 365 °F | B50 (50°C/h 50N); ISO 306 | ||
| Flammability, UL94 | HB | HB | UL94 | ||
| HB @Thickness 0.710 mm | HB @Thickness 0.0280 in | UL94 | |||
| Oxygen Index | 22.0 % | 22.0 % | ISO 4589 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| 65.0 - 93.0 °C | 149 - 199 °F | Cavity temperature | |||
| 219 °C | 426 °F | Ejection temperature; Internal | |||
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Rear Barrel Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Middle Barrel Temperature | 235 - 250 °C | 455 - 482 °F | |||
| Front Barrel Temperature | 240 - 260 °C | 464 - 500 °F | |||
| Nozzle Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |||
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 4 | 240 - 260 °C | 464 - 500 °F | |||
| Die Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Melt Temperature | 235 - 260 °C | 455 - 500 °F | |||
| 235 - 260 °C | 455 - 500 °F | ||||
| 260 °C | 500 °F | Injection molding; ISO 294 | |||
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |||
| 82.0 °C | 180 °F | Injection molding; ISO 294 | |||
| Injection Velocity | 300 mm/sec | 11.8 in/sec | ISO 294 | ||
| Drying Temperature | 120 - 130 °C | 248 - 266 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Moisture Content | 0.0200 % | 0.0200 % | Necessary low maximum residual | ||
| Hold Pressure | 48.0 MPa | 6960 psi | ISO 294 | ||
| Back Pressure | 0.000 - 0.345 MPa | 0.000 - 50.0 psi | |||
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Descriptive Properties | |||||
| Injection molding | Yes | ||||
| Injection speed | medium-fast | ||||
| Longer pre-drying times/storage | lower the temperature to 100° C until processed. | <= 60 h | |||
| Processing conditions | ISO 7792-2 | ||||
| Processing Notes | Fast Injection Speed | ||||
| Medium Screw Speed | |||||