- 熔體流動速率 [g/10min]: 75.0
- 密度 [g/cm3]: 1.26
- 缺口沖擊強度: 0.374
- 拉伸強度 [MPa]: 46.0
- 彎曲模量 [MPa]: 2.084
- 熱變形溫度 [℃]: 130.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ASTM D792 | ||
| Density | 1.26 g/cc | 0.0455 lb/in3 | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.0180 - 0.0200 cm/cm | 0.0180 - 0.0200 in/in | ASTM D955 | ||
| 0.0220 - 0.0330 cm/cm | 0.0220 - 0.0330 in/in | ISO 294-4 | |||
| Linear Mold Shrinkage, Transverse | 0.0220 - 0.0330 cm/cm | 0.0220 - 0.0330 in/in | ISO 294-4 | ||
| Melt Flow | 75.0 g/10 min | 75.0 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 46.0 MPa | 6670 psi | 50mm/min; ISO 527-2/1A | ||
| 57.2 MPa | 8300 psi | ASTM D638 | |||
| Elongation at Break | 250 % | 250 % | 50mm/min; ISO 527-2/1A | ||
| Elongation at Yield | 10.0 % | 10.0 % | 50mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 2.10 GPa | 305 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 63.0 MPa | 9140 psi | ISO 178 | ||
| 85.5 MPa | 12400 psi | ASTM D790 | |||
| Flexural Modulus | 2.084 GPa | 302.3 ksi | ISO 178 | ||
| 2.48 GPa @Temperature 22.8 °C | 360 ksi @Temperature 73.0 °F | ASTM D790 | |||
| Izod Impact, Notched | 0.374 J/cm | 0.700 ft-lb/in | ASTM D256 | ||
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU | ||
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.50 J/cm2 | 7.14 ft-lb/in2 | ISO 179/1eA | ||
| 0.690 J/cm2 @Temperature -30.0 °C | 3.28 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 | ||
| 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 | |||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Constant | 3.20 @Frequency 1.00e+6 Hz | 3.20 @Frequency 1.00e+6 Hz | ASTM D150 | ||
| 3.50 @Frequency 1.00e+6 Hz | 3.50 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| 4.00 @Frequency 100 Hz | 4.00 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 16.5 kV/mm | 420 kV/in | short term; ASTM D149 | ||
| 23.0 kV/mm | 584 kV/in | IEC 60243-1 | |||
| Dissipation Factor | 0.00200 @Frequency 1.00e+6 Hz | 0.00200 @Frequency 1.00e+6 Hz | ASTM D150 | ||
| 0.00700 @Frequency 100 Hz | 0.00700 @Frequency 100 Hz | IEC 60250 | |||
| 0.0200 @Frequency 1.00e+6 Hz | 0.0200 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | >= 600 V | >= 600 V | ASTM D3638 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| 225 °C | 437 °F | ASTM D3418 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | ISO 75-1, -2 | ||
| 224 °C | 435 °F | ASTM D648 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| 65.0 - 96.0 °C | 149 - 205 °F | Cavity temperature | |||
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |||
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 4 | 240 - 260 °C | 464 - 500 °F | |||
| Die Temperature | 240 - 260 °C | 464 - 500 °F | |||
| Melt Temperature | 243 °C | 469 °F | Injection molding; ISO 294 | ||
| 235 - 260 °C | 455 - 500 °F | ||||
| Mold Temperature | 82.0 °C | 180 °F | Injection molding; ISO 294 | ||
| Injection Velocity | 300 mm/sec | 11.8 in/sec | ISO 294 | ||
| Drying Temperature | 120 - 130 °C | 248 - 266 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Moisture Content | 0.0200 % | 0.0200 % | Necessary low maximum residual | ||
| Hold Pressure | 48.0 MPa | 6960 psi | ISO 294 | ||
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Descriptive Properties | |||||
| Injection molding | Yes | ||||
| Injection speed | medium-fast | ||||
| Longer pre-drying times/storage | lower the temperature to 100° C until processed. | <= 60 h | |||
| Processing conditions | ISO 7792-2 | ||||