- 吸水率 [%]: 0.06
- 缺口沖擊強(qiáng)度: 0.747
- 拉伸強(qiáng)度 [MPa]: 134.0
- 彎曲模量 [MPa]: 10.3
- 熱變形溫度 [℃]: 221.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.54 g/cc | 1.54 g/cc | ASTM D792 | ||
| Water Absorption | 0.060 % | 0.060 % | 24 hr. Immersion, -; ASTM D570 | ||
| 0.45 % | 0.45 % | Long-Term Immersion, -; ASTM D570 | |||
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 134 MPa | 19500 psi | Type 1 - Rigids, Break, 0.2 in/min; ASTM D638 | ||
| Elongation at Break | 2.0 % | 2.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 | ||
| Tensile Modulus | 13.1 GPa | 1900 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 | ||
| Flexural Strength | 200 MPa | 29000 psi | ASTM D790 | ||
| Flexural Modulus | 10.3 GPa | 1500 ksi | ASTM D790 | ||
| Compressive Strength | 152 MPa | 22000 psi | ASTM D695 | ||
| Izod Impact, Notched | 0.747 J/cm @Thickness 6.35 mm, Temperature 23.0 °C | 1.40 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F | Method A, Injection Molded; ASTM D256 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 221 °C | 430 °F | Annealed; ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 216 °C | 420 °F | Annealed; ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 249 - 266 °C | 480 - 510 °F | Molding | ||
| Mold Temperature | 121 °C | 250 °F | |||
| Drying Temperature | 107 °C | 225 °F | 4 hrs | ||
| Descriptive Properties | |||||
| Product Form | Pellets | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.