- 熔體流動速率 [g/10min]: 9.0
- 密度 [g/cm3]: 1.41
- 吸水率 [%]: 0.01
- 缺口沖擊強度: 0.747
- 彎曲模量 [MPa]: 5.40
- 熱變形溫度 [℃]: 213.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | ASTM D792 | ||
| Density | 1.41 g/cc | 0.0509 lb/in3 | ISO 1183 | ||
| Water Absorption | 0.0100 % | 0.0100 % | 24hr immersion; ASTM D570 | ||
| Moisture Absorption | 0.100 % | 0.100 % | 23°C/50%RH; ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.00300 - 0.00500 cm/cm | 0.00300 - 0.00500 in/in | ISO 294-4 | ||
| 0.00300 - 0.00700 cm/cm | 0.00300 - 0.00700 in/in | ASTM D955 | |||
| Melt Flow | 9.00 g/10 min | 9.00 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 90.0 | 90.0 | ISO 2039-2 | ||
| Tensile Strength at Break | 93.1 MPa | 13500 psi | ASTM D638 | ||
| 95.0 MPa | 13800 psi | 5mm/min; ISO 527-2/1A | |||
| Elongation at Break | 5.40 % | 5.40 % | 5mm/min; ISO 527-2/1A | ||
| 5.50 % @Temperature 22.8 °C | 5.50 % @Temperature 73.0 °F | ASTM D638 | |||
| Tensile Modulus | 5.20 GPa | 754 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 145 MPa | 21000 psi | ASTM D790 | ||
| 155 MPa | 22500 psi | ISO 178 | |||
| Flexural Modulus | 5.40 GPa | 783 ksi | ISO 178 | ||
| 4.83 GPa @Temperature 22.8 °C | 700 ksi @Temperature 73.0 °F | ASTM D790 | |||
| Izod Impact, Notched | 0.747 J/cm | 1.40 ft-lb/in | ASTM D256 | ||
| Izod Impact, Notched (ISO) | 5.30 kJ/m2 | 2.52 ft-lb/in2 | ISO 180/1A | ||
| Charpy Impact, Notched | 0.540 J/cm2 | 2.57 ft-lb/in2 | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | ASTM D257 | ||
| Dielectric Constant | 3.40 @Frequency 1000 Hz | 3.40 @Frequency 1000 Hz | ASTM D150 | ||
| Dielectric Strength | 18.1 kV/mm | 460 kV/in | short term; ASTM D149 | ||
| Dissipation Factor | 0.00200 @Frequency 1.00e+6 Hz | 0.00200 @Frequency 1.00e+6 Hz | ASTM D150 | ||
| Arc Resistance | 125 sec | 125 sec | ASTM D495 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 40.0 μm/m-°C | 22.2 μin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 110 μm/m-°C | 61.1 μin/in-°F | ISO 11359-2 | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| 225 °C | 437 °F | ASTM D3418 | |||
| Transformation Temperature, Tg | 60.0 °C | 140 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 213 °C | 415 °F | ASTM D648 | ||
| 217 °C | 423 °F | ISO 75-1, -2 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 189 °C | 372 °F | ISO 75-1, -2 | ||
| 192 °C | 378 °F | ASTM D648 | |||
| Flammability, UL94 | HB | HB | UL94 | ||
| HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | UL94 | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| 65.0 - 93.0 °C | 149 - 199 °F | Cavity temperature | |||
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Rear Barrel Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Middle Barrel Temperature | 235 - 250 °C | 455 - 482 °F | |||
| Front Barrel Temperature | 240 - 260 °C | 464 - 500 °F | |||
| Nozzle Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |||
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 4 | 240 - 260 °C | 464 - 500 °F | |||
| Die Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Melt Temperature | 235 - 260 °C | 455 - 500 °F | |||
| 235 - 260 °C | 455 - 500 °F | ||||
| 260 °C | 500 °F | Injection molding; ISO 294 | |||
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |||
| 82.0 °C | 180 °F | Injection molding; ISO 294 | |||
| Injection Velocity | 300 mm/sec | 11.8 in/sec | ISO 294 | ||
| Drying Temperature | 120 - 130 °C | 248 - 266 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Moisture Content | 0.0200 % | 0.0200 % | Necessary low maximum residual | ||
| Hold Pressure | 48.0 MPa | 6960 psi | ISO 294 | ||
| Back Pressure | 0.000 - 0.345 MPa | 0.000 - 50.0 psi | |||
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Descriptive Properties | |||||
| Injection molding | Yes | ||||
| Injection speed | medium-fast | ||||
| Longer pre-drying times/storage | lower the temperature to 100° C until processed. | <= 60 h | |||
| Processing conditions | ISO 7792-2 | ||||
| Processing Notes | Fast Injection Speed | ||||
| Medium Screw Speed | |||||