- 缺口沖擊強度: 1.9
- 拉伸強度 [MPa]: 53.1
- 彎曲模量 [MPa]: 2.07
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 | ||
| Linear Mold Shrinkage, Flow | 0.0070 - 0.0090 cm/cm | 0.0070 - 0.0090 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 53.1 MPa | 7700 psi | Type I, 5.1 mm/min; ASTM D638 | ||
| Elongation at Break | 100 % | 100 % | Type I, 5.1 mm/min; ASTM D638 | ||
| Flexural Strength | 75.8 MPa | 11000 psi | ASTM D790 | ||
| Flexural Modulus | 2.07 GPa | 300 ksi | ASTM D790 | ||
| Izod Impact, Notched | 1.90 J/cm @Thickness 3.18 mm, Temperature -20.0 °C | 3.56 ft-lb/in @Thickness 0.125 in, Temperature -4.00 °F | Injection Molded; ASTM D256A | ||
| 7.50 J/cm @Thickness 3.18 mm, Temperature 23.0 °C | 14.1 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | Injection Molded; ASTM D256A | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C @Thickness 6.35 mm | 212 °F @Thickness 0.250 in | Unannealed; ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 260 - 277 °C | 500 - 531 °F | |||
| Mold Temperature | 65.6 - 87.8 °C | 150 - 190 °F | |||
| Drying Temperature | 110 °C | 230 °F | |||
| Dry Time | 2.00 hour | 2.00 hour | |||
| Descriptive Properties | |||||
| Additive | UV Stabilizer | ||||
| Appearance | Black | ||||
| Forms | Pellets | ||||
| Generic Material | PC+PBT | ||||
| Generic Name | Polycarbonate + PBT (PC+PBT) | ||||
| Regional Availability | Africa & Middle East | ||||
| Asia Pacific | |||||
| Europe | |||||
| North America | |||||
| South America | |||||