- 缺口沖擊強度: 0.27
- 拉伸強度 [MPa]: 38.6
- 彎曲模量 [MPa]: 6.89
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 2.69 g/cc | 2.69 g/cc | ASTM D792 | ||
| Linear Mold Shrinkage, Flow | 0.011 - 0.017 cm/cm | 0.011 - 0.017 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 38.6 MPa | 5600 psi | Type I, 5.1 mm/min; ASTM D638 | ||
| Elongation at Break | 1.0 % | 1.0 % | Type I, 5.1 mm/min; ASTM D638 | ||
| Tensile Modulus | 6.89 GPa | 999 ksi | Type I, 5.1 mm/min; ASTM D638 | ||
| Flexural Strength | 68.9 MPa | 9990 psi | ASTM D790 | ||
| Flexural Modulus | 6.89 GPa | 999 ksi | ASTM D790 | ||
| Izod Impact, Notched | 0.270 J/cm @Thickness 6.35 mm, Temperature 23.0 °C | 0.506 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F | Injection Molded, Method A; ASTM D648 | ||
| Izod Impact, Unnotched | 2.40 J/cm @Thickness 3.18 mm, Temperature 23.0 °C | 4.50 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | Injection Molded; ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 249 - 266 °C | 480 - 511 °F | |||
| Mold Temperature | 82.2 - 121 °C | 180 - 250 °F | |||
| Drying Temperature | 107 °C | 225 °F | |||
| Descriptive Properties | |||||
| Appearance | White | ||||
| Features | High Specific Gravity | ||||
| Non-Toxic | |||||
| Forms | Pellets | ||||
| Generic Material | PBT | ||||
| Generic Name | Polybutylene Terephthalate (PBT) | ||||
| Processing Method | Injection Molding | ||||
| Regional Availability | Africa & Middle East | ||||
| Asia Pacific | |||||
| Europe | |||||
| North America | |||||
| South America | |||||
| Uses | Industrial Applications | ||||
| Medical/Healthcare Applications | |||||
| Sporting Goods | |||||