- 密度 [g/cm3]: 1.5
- 缺口沖擊強度: 0.427
- 拉伸強度 [MPa]: 57.9
- 彎曲模量 [MPa]: 4.14
- 熱變形溫度 [℃]: 188.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in3 | ASTM D792-91 |
| Viscosity Measurement | 1500 @Temperature 250 °C | 1500 @Temperature 482 °F | in-sec Melt Viscosity; 5.0 kg; ASTM D1238 Mod. |
| Linear Mold Shrinkage | 0.012 cm/cm | 0.012 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 57.9 MPa | 8400 psi | ASTM D638 |
| Flexural Modulus | 4.14 GPa | 600 ksi | ASTM D790 |
| Izod Impact, Notched | 0.427 J/cm | 0.800 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 188 °C | 370 °F | 1/4 inch bar; ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 238 - 254 °C | 460 - 490 °F | |
| Middle Barrel Temperature | 243 - 260 °C | 470 - 500 °F | |
| Front Barrel Temperature | 249 - 266 °C | 480 - 510 °F | |
| Nozzle Temperature | 243 - 260 °C | 470 - 500 °F | |
| Melt Temperature | 249 - 266 °C | 480 - 510 °F | |
| Mold Temperature | 71.1 - 93.3 °C | 160 - 200 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | |
| Moisture Content | 0.20 % | 0.20 % | |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |