- 密度 [g/cm3]: 1.46
- 拉伸強度 [MPa]: 65.0
- 熱變形溫度 [℃]: 160.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in3 | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.018 cm/cm @Thickness 2.00 mm | 0.018 in/in @Thickness 0.0787 in | Parallel; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.016 cm/cm @Thickness 2.00 mm | 0.016 in/in @Thickness 0.0787 in | Normal; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 65.0 MPa @Temperature 23.0 °C | 9430 psi @Temperature 73.4 °F | ISO 527 | ||
| Elongation at Break | 7.2 % @Temperature 23.0 °C | 7.2 % @Temperature 73.4 °F | nominal; ISO 527 | ||
| 9.0 % @Temperature 23.0 °C | 9.0 % @Temperature 73.4 °F | ISO 527 | |||
| Elongation at Yield | 4.6 % @Temperature 23.0 °C | 4.6 % @Temperature 73.4 °F | ISO 527 | ||
| Tensile Modulus | 3.00 GPa @Temperature 23.0 °C | 435 ksi @Temperature 73.4 °F | ISO 527 | ||
| Flexural Strength | 100 MPa @Temperature 23.0 °C | 14500 psi @Temperature 73.4 °F | ISO 178 | ||
| Charpy Impact Unnotched | 6.00 J/cm2 @Temperature 23.0 °C | 28.6 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.340 J/cm2 @Temperature -30.0 °C | 1.62 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | ||
| 0.380 J/cm2 @Temperature 23.0 °C | 1.81 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ISO 75-1/-2 | ||
| UL RTI, Electrical | 130 °C @Thickness 0.750 mm | 266 °F @Thickness 0.0295 in | UL 746B | ||
| UL RTI, Mechanical with Impact | 130 °C @Thickness 0.750 mm | 266 °F @Thickness 0.0295 in | UL 746B | ||
| UL RTI, Mechanical without Impact | 130 °C @Thickness 0.750 mm | 266 °F @Thickness 0.0295 in | UL 746B | ||
| Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | UL94 | ||
| V-0 @Thickness 0.750 mm | V-0 @Thickness 0.0295 in | UL94 | |||
| V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | UL94 | |||
| V-0 @Thickness 6.00 mm | V-0 @Thickness 0.236 in | UL94 | |||
| V-0 @Thickness 6.00 mm | V-0 @Thickness 0.236 in | IEC 60695-11-10 | |||
| V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | IEC 60695-11-10 | |||
| V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | IEC 60695-11-10 | |||
| V-0 @Thickness 0.750 mm | V-0 @Thickness 0.0295 in | IEC 60695-11-10 | |||
| Oxygen Index | 30 % | 30 % | ISO 4589-1/-2 | ||
| Glow Wire Test | 960 °C @Thickness 3.00 mm | 1760 °F @Thickness 0.118 in | IEC 60695-2-12 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 | ||
| 240 - 260 °C | 464 - 500 °F | Injection Molding | |||
| 250 °C | 482 °F | Optimum; Injection Molding | |||
| Mold Temperature | 80.0 °C | 176 °F | optimum; Injection Molding | ||
| 30.0 - 130 °C | 86.0 - 266 °F | Injection Molding | |||
| Drying Temperature | 110 - 130 °C | 230 - 266 °F | Injection Molding | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Injection Molding | ||
| Moisture Content | <= 0.040 % | <= 0.040 % | Injection Molding | ||
| Descriptive Properties | |||||
| Appearance | Black Color | ||||
| Features | Flame Retardant | ||||
| Forms | Pellets | ||||
| Generic | PBT | ||||
| Material Status | Preliminary Data | ||||
| Part Marking Code | >PBT-FR(17)< | ISO 11469 | |||
| Processing Method | Injection Molding | ||||
| Product Category | Flame Retardant Resins | ||||
| Flame Retardant Resins | |||||
| Unreinforced Resins | |||||
| Region Available - Global | Yes | ||||
| Resin Identification | PBT-FR(17) | ISO 1043 | |||
| RoHS Compliance | Contact Manufacturer | ||||