- 密度 [g/cm3]: 1.3
- 吸水率 [%]: 0.06
- 缺口沖擊強度: 0.44
- 斷裂伸長率 [%]: 75.0
- 彎曲強度 [MPa]: 50.0
- 彎曲模量 [MPa]: 2.20
- 熱變形溫度 [℃]: 155.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 - 1.32 g/cc | 0.0470 - 0.0477 lb/in3 | ASTM D792 |
| Water Absorption | 0.060 % | 0.060 % | 24 hour immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0080 - 0.020 cm/cm | 0.0080 - 0.020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 85 - 90 | 85 - 90 | ASTM D785 |
| Tensile Strength, Ultimate | 50.0 - 60.0 MPa | 7250 - 8700 psi | ASTM D638 |
| Elongation at Break | 50 - 90 % | 50 - 90 % | ASTM D638 |
| Flexural Yield Strength | 75.0 - 85.0 MPa | 10900 - 12300 psi | ASTM D790 |
| Flexural Modulus | 2.20 GPa | 319 ksi | ASTM D790 |
| Izod Impact, Notched | 0.440 - 0.540 J/cm @Thickness 6.35 mm | 0.824 - 1.01 ft-lb/in @Thickness 0.250 in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | ASTM D257 |
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | ASTM D257 |
| Dielectric Constant | 3.3 @Frequency 60 Hz | 3.3 @Frequency 60 Hz | ASTM D150 |
| Dielectric Strength | 20.0 kV/mm @Thickness 2.00 mm | 508 kV/in @Thickness 0.0787 in | ASTM D149 |
| Dissipation Factor | 0.0010 @Frequency 60 Hz | 0.0010 @Frequency 60 Hz | ASTM D150 |
| Arc Resistance | 120 sec | 120 sec | ASTM D495 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 90.0 μm/m-°C @Temperature 20.0 °C | 50.0 μin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Melting Point | 225 °C | 437 °F | DSC |
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | 1/32 in. |