- 密度 [g/cm3]: 1.41
- 彎曲強(qiáng)度 [MPa]: 17.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in3 | ISO 1183 |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | ASTM D551 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | ISO 527-1 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-1 |
| Tensile Modulus | 3.40 GPa | 493 ksi | ISO 527-1 |
| Thermal Properties | Metric | English | Comments |
| Specific Heat Capacity | 1.27 J/g-°C | 0.304 BTU/lb-°F | ASTM E1461 |
| Thermal Conductivity | 14.0 W/m-K | 97.2 BTU-in/hr-ft2-°F | ASTM E1461 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 200 - 210 °C | 392 - 410 °F | |
| Middle Barrel Temperature | 204 - 227 °C | 399 - 441 °F | |
| Front Barrel Temperature | 216 - 238 °C | 421 - 460 °F | |
| Melt Temperature | 216 - 238 °C | 421 - 460 °F | |
| Mold Temperature | 27.0 - 66.0 °C | 80.6 - 151 °F | |
| Drying Temperature | 82.0 °C | 180 °F | |
| Dry Time | 4 hour | 4 hour | |
| Dew Point | -18.0 °C | -0.400 °F | |
| Injection Pressure | 35.0 - 82.0 MPa | 5080 - 11900 psi | |
| Hold Pressure | 14.0 - 28.0 MPa | 2030 - 4060 psi | |
| Back Pressure | 0.000 - 0.350 MPa | 0.000 - 50.8 psi | |
| Screw Speed | 40 - 100 rpm | 40 - 100 rpm | |