- 密度 [g/cm3]: 1.41
- 缺口沖擊強度: 0.53
- 拉伸強度 [MPa]: 93.0
- 斷裂伸長率 [%]: 145
- 彎曲模量 [MPa]: 4.80
- 熱變形溫度 [℃]: 216.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in3 | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 93.0 MPa | 13500 psi | ASTM D638 |
| Flexural Yield Strength | 145 MPa | 21000 psi | ASTM D790 |
| Flexural Modulus | 4.80 GPa | 696 ksi | ASTM D790 |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 216 °C | 421 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 191 °C | 376 °F | ASTM D648 |