- 熔體流動速率 [g/10min]: 24.65
- 密度 [g/cm3]: 1.48
- 吸水率 [%]: 0.4
- 拉伸強度 [MPa]: 120.0
- 熱變形溫度 [℃]: 215.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in3 | ISO 1183 | ||
| Water Absorption | 0.40 % | 0.40 % | Saturation; DIN 53495/1L | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C; 50% RH | ||
| Viscosity Measurement | 92 | 92 | [ml/g]; Viscosity number; ISO 1628 | ||
| Linear Mold Shrinkage, Flow | 0.0027 cm/cm | 0.0027 in/in | 60x60x2 mm; ISO 294 | ||
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | 60x60x2 mm; ISO 294 | ||
| Melt Flow | 24.65 g/10 min @Load 2.16 kg, Temperature 275 °C | 24.65 g/10 min @Load 4.76 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 120 MPa | 17400 psi | 50 mm/min; ISO 527-2 | ||
| Elongation at Yield | 2.1 % | 2.1 % | 50 mm/min; ISO 527-2 | ||
| Modulus of Elasticity | 9.60 GPa | 1390 ksi | ISO 527-2 | ||
| Charpy Impact Unnotched | 5.00 J/cm2 | 23.8 ft-lb/in2 | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.700 J/cm2 | 3.33 ft-lb/in2 | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | 325 V | 325 V | Test solution A; IEC 112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 - 225 °C | 428 - 437 °F | DSC; ISO 11357-3 | ||
| Maximum Service Temperature, Air | 170 °C | 338 °F | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 187 °C | 369 °F | ISO 75-2 | ||
| Flammability, UL94 | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | |||
| HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 250 - 275 °C | 482 - 527 °F | Injection-molding | ||
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |||
| Descriptive Properties | |||||
| Color | Natural and Black | ||||
| Commercial Status | Europe | ||||