- 密度 [g/cm3]: 1.63
- 缺口沖擊強度: 0.75
- 彎曲強度 [MPa]: 119.0
- 彎曲模量 [MPa]: 13.0
- 硬度: 119.0
- 熱變形溫度 [℃]: 222.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.63 g/cc | 0.0589 lb/in3 | |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| Tensile Strength, Ultimate | 119 MPa | 17300 psi | ASTM D638 |
| Elongation at Break | 6.4 % | 6.4 % | ASTM D638 |
| Flexural Strength | 170 MPa | 24700 psi | ASTM D790 |
| Flexural Modulus | 13.0 GPa | 1890 ksi | ASTM D790 |
| Izod Impact, Notched | 0.750 J/cm | 1.41 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.34 J/cm | 10.0 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 210 - 225 °C | 410 - 437 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 222 °C | 432 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 240 °C | 464 °F | Approximate middle barrel temperature. |