- 拉伸強(qiáng)度 [MPa]: 1931.0
- 斷裂伸長(zhǎng)率 [%]: 1351
- 彎曲模量 [MPa]: 108.3
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 1931 MPa | 280100 psi | Room temperature |
| 1937 MPa @Temperature 71.0 °C | 280900 psi @Temperature 160 °F | 1/2 hr | |
| Tensile Modulus | 103.4 GPa | 15000 ksi | Room temperature |
| 110.3 GPa @Temperature 71.0 °C | 16000 ksi @Temperature 160 °F | 1/2 hr | |
| Flexural Yield Strength | 1351 MPa | 195900 psi | Room temperature |
| 1338 MPa @Temperature 71.0 °C | 194100 psi @Temperature 160 °F | 1/2 hr | |
| Flexural Modulus | 108.3 GPa | 15710 ksi | Room temperature |
| 117.2 GPa @Temperature 71.0 °C | 17000 ksi @Temperature 160 °F | 1/2 hr | |
| Compressive Yield Strength | 1158 MPa | 168000 psi | Room temperature |
| 1076 MPa @Temperature 71.0 °C | 156100 psi @Temperature 160 °F | 1/2 hr | |
| Compressive Modulus | 106.9 GPa | 15500 ksi | Room temperature |
| 93.1 GPa @Temperature 71.0 °C | 13500 ksi @Temperature 160 °F | 1/2 hr | |
| Shear Strength | 92.4 MPa | 13400 psi | Short Beam, Room temperature |
| 75.8 MPa @Temperature 71.0 °C | 11000 psi @Temperature 160 °F | Short Beam, 1/2 hr | |