- 拉伸強(qiáng)度 [MPa]: 28.3
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Viscosity | 75 cP @Temperature 82.2 °C | 75 cP @Temperature 180 °F | Part B; At Processing Temperature |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | >= 95 | >= 95 | ASTM D2240 |
| Hardness, Shore D | >= 50 | >= 50 | ASTM D2240 |
| Tensile Strength, Yield | 28.3 MPa | 4100 psi | ASTM D412 |
| Elongation at Break | 250 % | 250 % | ASTM D412 |
| Rebound | 30 % | 30 % | Bashore Rebound; ASTM D 2632 |
| Tear Strength | 39.4 kN/m | 225 pli | Split; ASTM D624 |
| Taber Abrasion, mg/1000 Cycles | 60 | 60 | ASTM D4060 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 82.2 °C | 180 °F | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 82.2 °C | 180 °F | |
| Mold Temperature | 82.2 °C | 180 °F | |
| Cure Time | 25.0 - 35.0 min | 0.417 - 0.583 hour | Demolding Time At 180°F Mold Temperature |
| Pot Life | 2.5 - 3.0 min | 2.5 - 3.0 min | At 180°F Mold Temperature |