- 拉伸強度 [MPa]: 29.0
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 65 | 65 | |
| 65 | 65 | heat aged 70 hours at 100oC | |
| Tensile Strength, Yield | 29.0 MPa | 4200 psi | |
| 29.56 MPa | 4288 psi | heat aged 70 hours at 100oC | |
| Elongation at Yield | 328 % | 328 % | heat aged 70 hours at 100oC |
| 362 % | 362 % | ||
| 100% Modulus | 0.00277 GPa | 0.402 ksi | |
| 200% Modulus | 0.00945 GPa | 1.37 ksi | |
| 300% Modulus | 0.02198 GPa | 3.188 ksi | |
| Tear Strength | 38.5 kN/m | 220 pli | |
| Compression Set | 16.8 % @Temperature 70.0 °C, Time 79200 sec | 16.8 % @Temperature 158 °F, Time 22.0 hour | heat aged 70 hours at 100oC |
| Processing Properties | Metric | English | Comments |
| Cure Time | 15.0 min @Temperature 155 °C | 0.250 hour @Temperature 311 °F | |