TSE Industries Millathane? 5004 Millable Polyurethane Elastomer with 20 PHR HAF Black (Typical)

TSE Industries Millathane? 5004 Millable Polyurethane Elastomer with 20 PHR HAF Black (Typical) 物性表: TSE Industries Millathane? 5004 Millable Polyurethane Elastomer with 20 PHR HAF Black (Typical)物性表及特性介紹,TSE Industries Millathane? 5004 Millable Polyurethane Elastomer with 20 PHR HAF Black (Typical)注塑參數(shù)詳情,如需TSE Industries Millathane? 5004 Millable Polyurethane Elastomer with 20 PHR HAF Black (Typical)下載, 可到相關(guān)下載區(qū)下載

拉伸強(qiáng)度 [MPa]: 16.5
脆化溫度 [℃]: -59.0

Physical Properties	Metric	English	Comments

Specific Gravity	1.28 g/cc	1.28 g/cc
Mooney Viscosity	70 @Temperature 100 °C	70 @Temperature 212 °F	ML 1+4

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	62	62	aged 70 hours at 250oF
	62	62	aged 70 hours at 300oF
	66	66	aged 7 days at Room Temp in ASTM Fuel A
	66	66	aged 70 hours at 250oF in ASTM Oil #903
	66	66	aged 96 hours at 158oF
	66	66
	67	67	aged 7 days at Room Temp in ASTM Fuel B
	67	67	aged 70 hours at 250oF in ASTM Oil #901
Tensile Strength, Yield	16.5 MPa	2400 psi	aged 7 days at Room Temp in ASTM Fuel B
	21.0 MPa	3050 psi	aged 70 hours at 300oF
	22.8 MPa	3300 psi	aged 70 hours at 250oF in ASTM Oil #901
	23.4 MPa	3400 psi	aged 70 hours at 250oF in ASTM Oil #903
	25.9 MPa	3750 psi	aged 7 days at Room Temp in ASTM Fuel A
	27.2 MPa	3950 psi	aged 70 hours at 250oF
	29.0 MPa	4200 psi
	29.3 MPa	4250 psi	aged 96 hours at 158oF
Elongation at Yield	300 %	300 %	aged 7 days at Room Temp in ASTM Fuel B
	370 %	370 %	aged 7 days at Room Temp in ASTM Fuel A
	400 %	400 %
	410 %	410 %	aged 70 hours at 250oF in ASTM Oil #903
	420 %	420 %	aged 70 hours at 250oF in ASTM Oil #901
	420 %	420 %	aged 70 hours at 250oF
	470 %	470 %	aged 96 hours at 158oF
	490 %	490 %	aged 70 hours at 300oF
100% Modulus	0.00352 GPa	0.510 ksi
200% Modulus	0.00979 GPa	1.42 ksi
300% Modulus	0.0121 GPa	1.75 ksi	aged 70 hours at 300oF
	0.0156 GPa	2.26 ksi	aged 70 hours at 250oF in ASTM Oil #901
	0.0157 GPa	2.28 ksi	aged 70 hours at 250oF in ASTM Oil #903
	0.0165 GPa	2.40 ksi	aged 7 days at Room Temp in ASTM Fuel B
	0.0179 GPa	2.60 ksi	aged 70 hours at 250oF
	0.0185 GPa	2.68 ksi	aged 96 hours at 158oF
	0.0186 GPa	2.70 ksi	aged 7 days at Room Temp in ASTM Fuel A
	0.0190 GPa	2.75 ksi
Tear Strength	550 kN/m	3140 pli	ASTM Die C
Compression Set	20 % @Temperature 70.0 °C, Time 79200 sec	20 % @Temperature 158 °F, Time 22.0 hour	Method B

Thermal Properties	Metric	English	Comments
Brittleness Temperature	-59.0 °C	-74.2 °F	Bell

Descriptive Properties
Bashore Resilience (%)	47
Gehman Modulus (oC)	-25.5		T2
	-33.1		T5
	-35		T10
	-39.5		T100
Mooney Scorch	25		t5, minutes; MS @ 121oC
Temperature of Retraction (oC)	-11		TR-50
	-23.7		TR-30
	-3.4		TR-70
	-33.4		TR-10
Volume Change (%)	-0.67		aged 70 hours at 250oF in ASTM Oil #901
	-1.03		aged 70 hours at 250oF in ASTM Oil #903
	1.3		aged 7 days at Room Temp in ASTM Fuel A
	16		aged 7 days at Room Temp in ASTM Fuel B

關(guān)鍵詞:
供應(yīng)
聚氨酯TS
TSE Industries Millathane? 5004 Millable Polyurethane Elastomer with 20 PHR HAF Black (Typical)

轉(zhuǎn)載請注明: 轉(zhuǎn)自中國塑膠原料之家 http://www.spnmy.cn/wuxingbiao/

本文鏈接: http://www.spnmy.cn/yuanliaoku/show-37351.html

免責(zé)聲明: 本文 TSE Industries Millathane? 5004 Millable Polyurethane Elastomer with 20 PHR HAF Black (Typical) 僅代表作者個人觀點(diǎn)，中國塑膠原料之家無關(guān)。中國塑膠原料之家網(wǎng)所轉(zhuǎn)載的內(nèi)容，其版權(quán)均由原作者和資料提供方所擁有！如因作品版權(quán)問題需要處理，請與我們聯(lián)絡(luò)