- 拉伸強(qiáng)度 [MPa]: 34.5
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | |
| Mooney Viscosity | 32 @Temperature 121 °C | 32 @Temperature 250 °F | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 65 | 65 | |
| Tensile Strength, Yield | 34.5 MPa | 5000 psi | |
| Elongation at Yield | 625 % | 625 % | |
| 100% Modulus | 0.00172 GPa | 0.250 ksi | |
| 300% Modulus | 0.00414 GPa | 0.600 ksi | |
| Tear Strength | 36.1 kN/m | 206 pli | Graves |
| Compression Set | 22 % | 22 % | Method B |
| Processing Properties | Metric | English | Comments |
| Cure Time | 90.0 min @Temperature 142 °C | 1.50 hour @Temperature 287 °F | |