- 缺口沖擊強度: 4.8
- 拉伸強度 [MPa]: 64.0
- 斷裂伸長率 [%]: 95.0
- 彎曲模量 [MPa]: 3.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Viscosity | 100 - 400 cP @Temperature 45.0 °C | 100 - 400 cP @Temperature 113 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 64.0 MPa | 9280 psi | Plain Cast Resin; ASTM D638 |
| Elongation at Break | 4.0 - 5.0 % | 4.0 - 5.0 % | Plain Cast Resin; ASTM D638 |
| Modulus of Elasticity | 2.80 GPa | 406 ksi | Plain Cast Resin; ASTM D638 |
| Flexural Yield Strength | 95.0 MPa | 13800 psi | Plain Cast Resin; ASTM D790 |
| Flexural Modulus | 3.00 GPa | 435 ksi | Plain Cast Resin; ASTM D790 |
| Izod Impact, Notched | 4.80 J/cm | 8.99 ft-lb/in | Plain Cast Resin; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C | 165 °F | Plain Cast Resin; ASTM D648 |
| Glass Transition Temp, Tg | 86.0 °C | 187 °F | Plain Cast Resin; ASTM D3418 |
| Processing Properties | Metric | English | Comments |
| Pot Life | 15.0 - 20.0 min @Temperature 23.0 °C | 15.0 - 20.0 min @Temperature 73.4 °F | |