- 拉伸強度 [MPa]: 34.5
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Solids Content | 7.5 % | 7.5 % | M201; by volume | ||
| 9.0 % | 9.0 % | M201; by weight | |||
| 52 % | 52 % | Mixed; by volume | |||
| 56 % | 56 % | Mixed; by weight | |||
| 67 % | 67 % | M331; by volume | |||
| 73 % | 73 % | M331; by weight | |||
| Volatile Organic Compounds (VOC) Content | 420 g/l | 420 g/l | |||
| Brookfield Viscosity | 0.89 cP @Temperature 25.0 °C | 0.89 cP @Temperature 77.0 °F | Part B, M201; LVT, Spindle #4 @ 30rpm | ||
| 8500 cP @Temperature 25.0 °C | 8500 cP @Temperature 77.0 °F | Part A, M331; LVT, Spindle #4 @ 30rpm | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 95 | 95 | |||
| Tensile Strength, Yield | 34.5 MPa | 5000 psi | ASTM D882-83, Method A | ||
| Elongation at Yield | 500 % | 500 % | ASTM D882-83, Method A | ||
| Taber Abrasion, mg/1000 Cycles | 0.00 | 0.00 | CS17 1000g/1000cycles; ASTM D4060 | ||
| 60 | 60 | H18 1000g/1000 cycles; ASTM D4060 | |||
| Thermal Properties | Metric | English | Comments | ||
| Flash Point | 33.9 °C | 93.0 °F | Part A, M331; Setaflash | ||
| 43.3 °C | 110 °F | Part B, M201; Setaflash | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 15.0 - 30.0 min | 0.250 - 0.500 hour | Set to Touch | ||
| 60.0 - 120 min | 1.00 - 2.00 hour | Surface Dry | |||
| 240 - 360 min | 4.00 - 6.00 hour | Dry Hard | |||
| Pot Life | 120 min @Temperature 25.0 °C | 120 min @Temperature 77.0 °F | 50% relative humidity | ||
| Shelf Life | 6.00 Month @Temperature 24.0 °C | 6.00 Month @Temperature 75.2 °F | Part A, M331 | ||
| 6.00 Month @Temperature 24.0 °C | 6.00 Month @Temperature 75.2 °F | Part B, M201 | |||
| Descriptive Properties | |||||
| Appearance | Black | Part A, M331 | |||
| Black | Mixed | ||||
| Yellow to Dark Amber | Part B, M201 | ||||
| Weight per Gallon (lbs) | 7 | Part B, M201 | |||
| 8.4 | Part A, M331 | ||||