- 吸水率 [%]: 0.3
- 拉伸強度 [MPa]: 0.689
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 0.950 g/cc | 0.950 g/cc | STM 2 | ||
| Water Absorption | 0.30 % @Temperature 25.0 °C, Time 605000 sec | 0.30 % @Temperature 77.0 °F, Time 168 hour | ASTM D570 | ||
| Loss On Ignition | 0.050 % @Temperature 100 °C, Time 86400 sec | 0.050 % @Temperature 212 °F, Time 24.0 hour | |||
| Viscosity | 750 cP @Temperature 25.0 °C | 750 cP @Temperature 77.0 °F | Mixed; STM 1 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 12 | 12 | ASTM D2240 | ||
| Tensile Strength, Yield | 0.689 MPa | 100 psi | ASTM D638 | ||
| Elongation at Yield | >= 250 % | >= 250 % | ASTM D638 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 5.00e+13 ohm-cm @Temperature 130 °C | 5.00e+13 ohm-cm @Temperature 266 °F | ASTM D257 | ||
| 4.00e+14 ohm-cm @Temperature 105 °C | 4.00e+14 ohm-cm @Temperature 221 °F | ASTM D257 | |||
| 2.00e+16 ohm-cm @Temperature 25.0 °C | 2.00e+16 ohm-cm @Temperature 77.0 °F | ASTM D257 | |||
| Dielectric Constant | 3.1 @Frequency 1.00e+6 Hz, Temperature 25.0 °C | 3.1 @Frequency 1.00e+6 Hz, Temperature 77.0 °F | ASTM D150 | ||
| Dissipation Factor | 0.20 @Frequency 1.00e+6 Hz, Temperature 25.0 °C | 0.20 @Frequency 1.00e+6 Hz, Temperature 77.0 °F | ASTM D150 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 130 °C | 266 °F | |||
| Glass Transition Temp, Tg | -72.0 °C | -97.6 °F | ASTM D3418 | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 30.0 min @Temperature 25.0 °C | 0.500 hour @Temperature 77.0 °F | Initial | ||
| 5760 min @Temperature 25.0 °C | 96.0 hour @Temperature 77.0 °F | Full | |||
| Pot Life | 4.0 - 5.0 min @Temperature 25.0 °C | 4.0 - 5.0 min @Temperature 77.0 °F | |||
| Shelf Life | 6.00 Month @Temperature 25.0 °C | 6.00 Month @Temperature 77.0 °F | |||
| Descriptive Properties | |||||
| Appearance | Clear | ||||
| Mix Ratio | 1:1 | by volume | |||
| 100:107 | by weight | ||||
| Thermal Shock | Excellent | ||||