- 密度 [g/cm3]: 1.07
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.07 g/cc | 0.0385 lb/in3 | |||
| Viscosity | 40000 cP | 40000 cP | Mixed Viscosity | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 86 | 86 | Cured; ASTM D2240 | ||
| Tensile Strength at Break | 24.1 MPa | 3500 psi | ASTM D412 | ||
| Elongation at Break | <= 600 % | <= 600 % | ASTM D412 | ||
| Tear Strength | 70.1 kN/m | 400 pli | ASTM D624 | ||
| Taber Abrasion, mg/1000 Cycles | 90 | 90 | H-18 wheel (1000 gram load) | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 13.4 kV/mm | 340 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 48.9 °C | 120 °F | wet | ||
| 82.2 °C | 180 °F | dry | |||
| Shrinkage | 23 % | 23 % | Cured (shrinkage due to solvent loss); ASTM D2566 | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 1440 min | 24.0 hour | Functional cure | ||
| Pot Life | 45 min | 45 min | at 75°F | ||
| Descriptive Properties | |||||
| Coverage per pound, in2 @ 1/4" thickness | 104 | ||||
| Mix ratio by weight (Resin:Hardener) | 80:20 | ||||