- 密度 [g/cm3]: 1.04
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.04 g/cc | 0.0377 lb/in3 | |||
| Viscosity | 10000 cP | 10000 cP | Mixed Viscosity | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 87 | 87 | Cured; ASTM D2240 | ||
| Tensile Strength at Break | 14.5 MPa | 2100 psi | ASTM D412 | ||
| Elongation at Break | <= 650 % | <= 650 % | ASTM D412 | ||
| Tear Strength | 61.4 kN/m | 350 pli | ASTM D624 | ||
| Taber Abrasion, mg/1000 Cycles | 285 | 285 | H-18 wheel (1000 gram load) | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 13.8 kV/mm | 350 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 48.9 °C | 120 °F | wet | ||
| 82.2 °C | 180 °F | dry | |||
| Shrinkage | 0.18 % | 0.18 % | Cured; ASTM D2566 | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 960 min | 16.0 hour | Functional cure | ||
| Pot Life | 30 min | 30 min | at 75°F | ||
| Descriptive Properties | |||||
| Coverage per pound, in2 @ 1/4" thickness | 106 | ||||
| Demolding Time, hours | 10 | ||||
| Mix ratio by weight (Resin:Hardener) | 77:23 | ||||