- 密度 [g/cm3]: 1.14
- 吸水率 [%]: 2.6
- 缺口沖擊強度: 4.3
- 彎曲強度 [MPa]: 19.0
- 彎曲模量 [MPa]: 0.690
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in3 | ASTM D792 |
| Water Absorption at Saturation | 2.6 % | 2.6 % | 240 hours; Bayer Test |
| Linear Mold Shrinkage | 0.0070 cm/cm | 0.0070 in/in | Bayer Test |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 60 | 60 | ASTM D2240 |
| Tensile Strength, Ultimate | 19.0 MPa | 2760 psi | ASTM D638/D412 |
| Elongation at Break | 200 % | 200 % | ASTM D638/D412 |
| Flexural Modulus | 0.690 GPa | 100 ksi | ASTM D790 |
| Izod Impact, Notched | 4.30 J/cm | 8.06 ft-lb/in | ASTM D256 |
| Tear Strength | 110 kN/m | 628 pli | Die C; ASTM D624 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 79.2 μm/m-°C @Temperature 20.0 °C | 44.0 μin/in-°F @Temperature 68.0 °F | ASTM D696 |