- 密度 [g/cm3]: 1.116
- 彎曲強度 [MPa]: 18.8
- 脆化溫度 [℃]: -43.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.116 g/cc | 0.04032 lb/in3 | |
| Mooney Viscosity | 82 @Temperature 100 °C | 82 @Temperature 212 °F | ML 1 + 4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 75 | 75 | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tensile Strength, Ultimate | 18.8 MPa | 2730 psi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Elongation at Break | 155 % | 155 % | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 50% Modulus | 0.00380 GPa | 0.551 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| 100% Modulus | 0.0104 GPa | 1.51 ksi | Vulcanizate, Press cured, TC95 +3min at 160°C |
| Tear Strength | 17.0 kN/m | 97.0 pli | Die C, Vulcanizate, Press cured, TC95 +3min at 160°C |
| Compression Set | 7.0 % @Temperature 125 °C | 7.0 % @Temperature 257 °F | Pellets cured MDR TC95 + 15 min at 160°C, 70 hr at 125°C; Method B |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -43.0 °C | -45.4 °F | Temperature Retraction, TR-10 |