- 彎曲強度 [MPa]: 18.3
- 脆化溫度 [℃]: -23.9
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Mooney Viscosity | 64 @Temperature 121 °C | 64 @Temperature 250 °F | ML-10 (gum) |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 71 | 71 | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Tensile Strength, Ultimate | 18.3 MPa | 2650 psi | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Elongation at Break | 207 % | 207 % | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Modulus of Elasticity | 0.000800 GPa | 0.116 ksi | 10% Modulus, Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| 100% Modulus | 0.00660 GPa | 0.957 ksi | Cured 7 min at 177°C and Post Cured 2 hr at 232°C |
| Compression Set | 11 % @Temperature 200 °C | 11 % @Temperature 392 °F | Method B, O-rings 22 hr at 200°C (Post Cured 2 hr at 232°C) |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -23.9 °C | -11.0 °F | TR-10 |
| Glass Transition Temp, Tg | -25.7 °C | -14.3 °F | DSC |