- 彎曲強度 [MPa]: 14.1
- 脆化溫度 [℃]: -16.0
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 81 | 81 | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D2240-91 |
| Tensile Strength, Ultimate | 14.1 MPa | 2050 psi | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412-92 |
| Elongation at Break | 165 % | 165 % | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412-92 |
| 100% Modulus | 0.00920 GPa | 1.33 ksi | Cured 10 min at 177°C and Post Cured 24 hr at 232°C; ASTM D412-92 |
| Tear Strength | 27.7 kN/m | 158 pli | Die C, Cured 10 min at 177°C and Post Cured 24 hr at 232°C |
| Compression Set | 19 % @Temperature 200 °C | 19 % @Temperature 392 °F | Method B, O-rings 70 hr; ASTM D1414-94 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -16.0 °C | 3.20 °F | Temperature Retraction, TR-10, using 50% elongation; ASTM D1329-88 |