- 拉伸強度 [MPa]: 9.3
- 彎曲強度 [MPa]: 16.2
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Viscosity Measurement | 6.8 @Temperature 160 °C | 6.8 @Temperature 320 °F | [min]; ts1, (1 RAD); ASTM D2084 | ||
| 10.1 @Temperature 160 °C | 10.1 @Temperature 320 °F | [min]; T50, (1 RAD); ASTM D2084 | |||
| 10.2 @Temperature 160 °C | 10.2 @Temperature 320 °F | [dNm]; ML, (1 RAD); ASTM D2084 | |||
| 13.3 @Temperature 160 °C | 13.3 @Temperature 320 °F | [min]; T90, (1 RAD); ASTM D2084 | |||
| 40 @Temperature 160 °C | 40 @Temperature 320 °F | [dNm]; MH, (1 RAD); ASTM D2084 | |||
| Mooney Viscosity | 45 @Temperature 100 °C | 45 @Temperature 212 °F | [MU]; ML 1+4; ASTM D1646 | ||
| Ash | 0.030 % | 0.030 % | ASTM D1416 | ||
| Collected Volatile Condensable Material | 0.20 % | 0.20 % | ASTM D1416 | ||
| Storage Temperature | <= 30.0 °C | <= 86.0 °F | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 16.2 MPa | 2350 psi | Die C (35 min / 145°C); ASTM D412 | ||
| Tensile Strength, Yield | 9.30 MPa @Strain 300 % | 1350 psi @Strain 300 % | ASTM D412 | ||
| Elongation at Break | 492 % | 492 % | ASTM D412 | ||
| Processing Properties | Metric | English | Comments | ||
| Shelf Life | >= 12.0 Month | >= 12.0 Month | |||
| Descriptive Properties | |||||
| Accelerator (TBBS) wt% | 0.9 | ASTM D3189 | |||
| Carbon Black wt% | 60 | ASTM D3189; IRB 6 | |||
| Cis-1,4 Content % | 97 | Supplier Method (NMR) | |||
| Dry Gel Content mg/kg | 200 | Supplier Method | |||
| Naphthenic oil type 103 wt% | 15 | ASTM D226 | |||
| Stearic Acid wt% | 2 | ASTM D3189 | |||
| Sulfur content, % | 1.5 | ASTM D3189 | |||
| Zinc Oxide wt% | 3 | ASTM D3189 | |||