- 密度 [g/cm3]: 1.25
- 吸水率 [%]: 0.1
- 缺口沖擊強度: 0.8
- 彎曲強度 [MPa]: 38.0
- 彎曲模量 [MPa]: 1.72
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in3 | ASTM D792 |
| Water Absorption at Saturation | 0.10 % | 0.10 % | 240 hours; Bayer Test |
| Linear Mold Shrinkage | 0.0043 cm/cm | 0.0043 in/in | Bayer Test |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 38.0 MPa | 5510 psi | ASTM D638/D412 |
| Elongation at Break | 40 % | 40 % | ASTM D638/D412 |
| Flexural Modulus | 1.72 GPa | 249 ksi | ASTM D790 |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Tear Strength | 97.0 kN/m | 553 pli | Die C; ASTM D624 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 68.0 μm/m-°C @Temperature 20.0 °C | 37.8 μin/in-°F @Temperature 68.0 °F | ASTM D696 |