- 密度 [g/cm3]: 1.23
- 拉伸強度 [MPa]: 8.1
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in3 | ASTM D3165 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 41 | 41 | ASTM D2240 | ||
| 29.725 @Treatment Temp. 200 °C, Time 252000 sec | 29.725 @Treatment Temp. 392 °F, Time 70.0 hour | Heat Aging; ASTM D573 | |||
| Tensile Strength, Yield | 8.10 MPa | 1170 psi | ASTM D412 | ||
| 9.60 MPa @Treatment Temp. 200 °C, Time 252000 sec | 1390 psi @Treatment Temp. 392 °F, Time 70.0 hour | Heat Aging; ASTM D573 | |||
| Elongation at Break | 727.6 % | 727.6 % | ASTM D412 | ||
| 552.976 % @Treatment Temp. 200 °C, Time 252000 sec | 552.976 % @Treatment Temp. 392 °F, Time 70.0 hour | Heat Aging; ASTM D573 | |||
| Compressive Modulus | 0.000390 GPa @Strain 5.00 % | 0.0566 ksi @Strain 5.00 % | |||
| 0.000620 GPa @Strain 10.0 % | 0.0899 ksi @Strain 10.0 % | ||||
| 0.00131 GPa @Strain 20.0 % | 0.190 ksi @Strain 20.0 % | ||||
| 0.00202 GPa @Strain 25.0 % | 0.293 ksi @Strain 25.0 % | ||||
| Compression Set | 6.36 % @Temperature 175 °C, Time 79200 sec | 6.36 % @Temperature 347 °F, Time 22.0 hour | ASTM D395 | ||
| Descriptive Properties | |||||
| Color | Red | ||||