- 密度 [g/cm3]: 1.219
- 拉伸強度 [MPa]: 16.8
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.219 g/cc | 0.04404 lb/in3 | ASTM D3165 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 69 | 69 | ASTM D2240 | ||
| 75.97 @Treatment Temp. 100 °C, Time 252000 sec | 75.97 @Treatment Temp. 212 °F, Time 70.0 hour | Heat Aging; ASTM D573 | |||
| Tensile Strength, Yield | 16.8 MPa | 2440 psi | ASTM D412 | ||
| 15.792 MPa @Treatment Temp. 100 °C, Time 252000 sec | 2290.4 psi @Treatment Temp. 212 °F, Time 70.0 hour | Heat Aging; ASTM D573 | |||
| Elongation at Break | 433.6 % | 433.6 % | ASTM D412 | ||
| 305.86 % @Treatment Temp. 100 °C, Time 252000 sec | 305.86 % @Treatment Temp. 212 °F, Time 70.0 hour | Heat Aging; ASTM D573 | |||
| Compressive Modulus | 0.000590 GPa @Strain 5.00 % | 0.0856 ksi @Strain 5.00 % | |||
| 0.00101 GPa @Strain 10.0 % | 0.146 ksi @Strain 10.0 % | ||||
| 0.00159 GPa @Strain 20.0 % | 0.231 ksi @Strain 20.0 % | ||||
| 0.00210 GPa @Strain 25.0 % | 0.305 ksi @Strain 25.0 % | ||||
| Compression Set | 6.44 % @Temperature 100 °C, Time 79200 sec | 6.44 % @Temperature 212 °F, Time 22.0 hour | ASTM D395 | ||
| Descriptive Properties | |||||
| Color | Black | ||||