- 密度 [g/cm3]: 1.4
- 吸水率 [%]: 0.35
- 缺口沖擊強度: 0.27
- 斷裂伸長率 [%]: 83.0
- 彎曲強度 [MPa]: 59.0
- 彎曲模量 [MPa]: 7.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in3 | ASTM D792 |
| Apparent Bulk Density | 0.550 g/cc | 0.0199 lb/in3 | ASTM D1895 |
| Water Absorption | 0.35 % | 0.35 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | Compression; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 85 | 85 | ASTM D785 |
| Tensile Strength, Ultimate | 59.0 MPa | 8560 psi | ASTM D638 |
| Flexural Yield Strength | 83.0 MPa | 12000 psi | ASTM D790 |
| Flexural Modulus | 7.00 GPa | 1020 ksi | ASTM D790 |
| Compressive Yield Strength | 234 MPa | 33900 psi | ASTM D695 |
| Izod Impact, Notched | 0.270 J/cm | 0.506 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 2.30e+11 ohm-cm | 2.30e+11 ohm-cm | ASTM D257 |
| Dielectric Strength | 11.4 kV/mm | 290 kV/in | ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 185 °C | 365 °F | ASTM D648 |